Detecting the Oxidation of Zircaloy Claddings by Infrared Interference
Abstract
As the expected life of dry cask storage installations increases, it becomes increasingly desirable to monitor the state and performance of the cask internals to ensure that they continue to safely contain the radioactive materials in the fuel. One aspect of this task is the monitoring of oxidation of the cladding. With this consideration in mind, Zircaloy-4 (Zr-4) cladding samples were exposed to air at 500C for various duration times to create thin corrosion oxide layers on the surface. The surfaces of the oxidized samples were then systematically scanned by Fourier Transform Infrared (FT-IR) spectroscopy to achieve the infrared (IR) interference spectra and study the relationship between the optical interference and the various thicknesses of the oxide layers. The profiles of the oxide layers were verified througth cross-sectional examination by Scanning Electron Microscopy. The IR interference patterns varied with oxide layer thickness, enabling the determination of oxide layer thickness of values, including half micron thick. Further analysis demonstrated that the interference oscillation period and the oscillation amplitude decreased with increasing oxide layer thickness. Combined with a physical model that describes the optical interference, the interference spectra were directly correlated to the oxide layer thickness quantitatively. The study provides the basis for an accurate, nondestructive and sensitive method to monitor the degree of zirconium-based cladding corrosion due to oxidation.
References
- 1.
National Research Council . Safety and Security of Commercial Spent Nuclear Fuel Storage: Public Report (The National Academies Press, Washington, DC, 2006). Google Scholar - 2. , Nucl. Technol. 32, 60 (1977). Web of Science, Google Scholar
- 3. , J. Nucl. Mater. 82, 84 (1979). Web of Science, Google Scholar
- 4. , J. Nucl. Mater. 140, 32 (1986). Web of Science, Google Scholar
- 5. , J. Nucl. Mater. 336, 331 (2005). Web of Science, Google Scholar
- 6. , NDT&E INTL. 44, 555 (2010). Web of Science, Google Scholar
- 7. , NDT&E INTL. 42, 150 (2009). Web of Science, Google Scholar
- 8. , Key Eng. Mater. 340, 229 (2007). Google Scholar
- 9. , Int. J. Pressure Vessels Piping 41, 113 (1990). Web of Science, Google Scholar
- 10. , Ultrasonics 31, 3 (1993). Web of Science, Google Scholar
- 11. , J. Appl. Phys. 45, 5B (2006). Web of Science, Google Scholar
- 12. , Review of Progress in Quantitative Non-destructive Evaluation 27 (American Institute of Physics, Melville, NY, 2008). Google Scholar
- 13. , IEEE Trans. Magn. 30, 6 (1994). Google Scholar
- 14. , NDT&E INTL. 30, 1 (1997). Web of Science, Google Scholar
- 15. , IEEE Trans. Magn. 28, 5 (1992). Web of Science, Google Scholar
- 16. , Sci. Mater. 57, 813 (2007). Web of Science, Google Scholar
- 17. , NDT&E 24, 1 (2009). Google Scholar
- 18. , J. Soc. Mater. Sci. (Japan) 33, 1097 (1984). Google Scholar
- 19. , J. Eng. Mater. Technol. 111, 1 (1989). Web of Science, Google Scholar
- 20. , J. Mater. Sci. Lett. 18, 1175 (1999). Web of Science, Google Scholar
- 21. , Trans. AIME 185, 515 (1949). Google Scholar
- 22. , Continuous measurement of Zircaloy corrosion in air with an ultrasonic corrosion monitor, IEEE 1984 Ultrasonics Symposium,
Dallas, Texas, USA ,November 1984 , p. 860. Google Scholar - 23. , Nucl. Instrum. Methods Phys. Res. B Beam Interactions Mater. Atoms 181, 640 (2001). Web of Science, Google Scholar
- 24. , Corrosion 37, 575 (1981). Web of Science, Google Scholar
- 25. , J. Nucl. Mater. 175, 237 (1990). Web of Science, Google Scholar
- 26. , J. Nucl. Mater. 445, 7 (2014). Web of Science, Google Scholar
- 27. , J. Nucl. Mater. 421, 160 (2012). Web of Science, Google Scholar
- 28. , J. Nucl. Mater. 199, 258 (1993). Web of Science, Google Scholar
- 29. , Microchim. Acta 104, 1 (1991). Google Scholar
- 30. , J. Phys. E: Sci. Instrum. 9, 1002 (1976). Google Scholar
- 31. , Zirconium in the nuclear Industry, 11th Int. Symp.,
Garmisch-Partenkirche, Germany , ASTM STP 1295, 218 (1996). Google Scholar - 32. , J. Am. Ceram. Soc. 54, 254 (1971). Web of Science, Google Scholar
- 33. , Appl. Opt. 19, 3245 (1980). Web of Science, Google Scholar