World Scientific
  • Search
Skip main navigation

Cookies Notification

We use cookies on this site to enhance your user experience. By continuing to browse the site, you consent to the use of our cookies. Learn More
Our website is made possible by displaying certain online content using javascript.
In order to view the full content, please disable your ad blocker or whitelist our website

System Upgrade on Tue, Oct 25th, 2022 at 2am (EDT)

Existing users will be able to log into the site and access content. However, E-commerce and registration of new users may not be available for up to 12 hours.
For online purchase, please visit us again. Contact us at [email protected] for any enquiries.


    The Co-Ni alloy nanowires were electrodeposited into porous anodic aluminum oxide (AAO) templates. At the first, highly ordered AAO templates were synthesized by two-step anodizing of aluminum to increase pore ordering. Arrays of nanowires with diameter about 30 nm and length about 5000 nm were electrodeposited by alternating current. The composition and structure property of nanowires were investigated by EDX, SEM and TEM techniques. It was found that nanowire composition was related to ions concentration in solution and it was shown that at the optimum potential range of electrodeposition (17-19 V), a change at the potential was shown no strong effect on chemical composition of nanowires. It was observed that nano pores were filled continuously and so nanowires were dense with uniform composition in nanowire length.